ICC 717 Ultimate Black

International Coatings 717 Ultimate Black


717 Ultimate Black™ is a non-phthalate, high pigment, fast flashing, low tack, high performance plastisol screen printing ink.

717 Ultimate Black™ provides a deep black color that is very creamy, short bodied and is easy to print on automatic or manual presses.

717 Ultimate Black™ achieves excellent penetration into fabrics when printing through fine mesh counts.


717 Ultimate Black™ will spot dry, with a very low after flash tack. Dwell time is dependent on the spot dryer used. In some cases, you may have to lower the heat of the spot cure unit because too much heat may actually make the ink tacky. When you spot dry, you are only partially fusing or gelling the surface of the ink. The ink should be just dry to the touch, with no lift-off, but not totally fused. Final fusing or curing should occur in the dryer.


717 Ultimate Black™ was formulated to make printing opaque black easy, so hand printing is less tiring. The result is improved operator performance. Automatic equipment can be adjusted to lower pressure settings, thus improving screen life and squeegee durability.

717 Ultimate Black™ prints so easily that a finer screen mesh can be used to achieve the same opacity as what you would expect from other opaque black inks at lower mesh counts.

717 Ultimate Black™ is not a color-mixing black ink.

Fibrillation can occur when printing on some cotton fabrics, especially when printing through finer mesh counts.

Adding any reducers or additives can lower bleed resistance, reduce opacity, or increase cure times of the ink. Stir the ink prior to printing on press and after addition of reducers or additives.

Test dryer temperatures and wash test printed product before and during a production run.

Write Your Own Review
You're reviewing:ICC 717 Ultimate Black
Your Rating
Brand Description
History Color sit amet, consectetur adipiscing elit. In gravida pellentesque ligula, vel eleifend turpis blandit vel. Nam quis lorem ut mi mattis ullamcorper ac quis dui. Vestibulum et scelerisque ante, eu sodales mi. Nunc tincidunt tempus varius. Integer ante dolor, suscipit non faucibus a, scelerisque vitae sapien.